|Year : 2016 | Volume
| Issue : 1 | Page : 62
Bone repair with differentiated osteoblasts from adipose-derived stem cells in hydroxyapatite/tricalcium phosphate in vivo
Batool Hashemibeni1, Leila Dehghani2, Farzaneh Sadeghi1, Ebrahim Esfandiari1, Masood Gorbani3, Ali Akhavan4, Soheil T Tahani5, Hamid Bahramian1, Vahid Goharian6
1 Department of Anatomical Sciences, Faculty of Medicine, Isfahan University of Medical Sciences, Isfahan, Iran
2 Department of Medical Sciences, Islamic Azad University, Najafabad Branch, Isfahan, Iran
3 Department of Tissue Engineering and Cell Therapy, Tehran University of Medical Sciences; Applied Biotechnology Center, Pajooheshgah Baqiatallah University and Medical Sciences, Tehran, Iran
4 Torabinegad Dental Research Center, Dental School, Isfahan University of Medical Sciences, Isfahan, Iran
5 Department of Medical Sciences, Islamic Azad University, Najafabad Branch; Isfahan Neurosciences Research Center, Al Zahra Hospital, Isfahan University of Medical Sciences, Isfahan, Iran
6 Department of Surgery, Amine Hospital; Institute of Novin Tahlilgarane Nesfe-jahan, Isfahan, Iran
|Date of Submission||29-Oct-2014|
|Date of Acceptance||07-Nov-2015|
|Date of Web Publication||01-Apr-2016|
Department of Anatomical Sciences, Faculty of Medicine, Isfahan University of Medical Sciences, Isfahan
Source of Support: None, Conflict of Interest: None
Background: Recently, tissue engineering has developed approaches for repair and restoration of damaged skeletal system based on different scaffolds and cells. This study evaluated the ability of differentiated osteoblasts from adipose-derived stem cells (ADSCs) seeded into hydroxyapatite/tricalcium phosphate (HA-TCP) to repair bone.
Methods: In this study, ADSCs of 6 canines were seeded in HA-TCP and differentiated into osteoblasts in osteogenic medium in vitro and bone markers evaluated by reverse transcription polymerase chain reaction (RT-PCR). Scanning electron microscopy (SEM) was applied for detection of cells in the pores of scaffold. HA-TCP with differentiated cells as the test group and without cells as the cell-free group were implanted in separate defected sites of canine's tibia. After 8 weeks, specimens were evaluated by histological, immunohistochemical methods, and densitometry test. The data were analyzed using the SPSS 18 version software.
Results: The expression of Type I collagen and osteocalcin genes in differentiated cells were indicated by RT-PCR. SEM results revealed the adhesion of cells in scaffold pores. Formation of trabecular bone confirmed by histological sections that revealed the thickness of bone trabecular was more in the test group. Production of osteopontin in extracellular matrix was indicated in both groups. Densitometry method indicated that strength in the test group was similar to cell-free group and natural bone (P > 0.05).
Conclusions: This research suggests that ADSCs-derived osteoblasts in HA-TCP could be used for bone tissue engineering and repairing.
Keywords: Adipose-derived stem cells, animal model, bone repair, hydroxyapatite/tricalcium phosphate
|How to cite this article:|
Hashemibeni B, Dehghani L, Sadeghi F, Esfandiari E, Gorbani M, Akhavan A, Tahani ST, Bahramian H, Goharian V. Bone repair with differentiated osteoblasts from adipose-derived stem cells in hydroxyapatite/tricalcium phosphate in vivo. Int J Prev Med 2016;7:62
|How to cite this URL:|
Hashemibeni B, Dehghani L, Sadeghi F, Esfandiari E, Gorbani M, Akhavan A, Tahani ST, Bahramian H, Goharian V. Bone repair with differentiated osteoblasts from adipose-derived stem cells in hydroxyapatite/tricalcium phosphate in vivo. Int J Prev Med [serial online] 2016 [cited 2020 Jan 19];7:62. Available from: http://www.ijpvmjournal.net/text.asp?2016/7/1/62/179510
| Introduction|| |
Since large bone lesions never heal spontaneously, the repair and regeneration of bone defects is a major clinical challenge. , Currently, autograft, allograft, xenograft, and Allizarov methods have been used for the bone repair. , These methods have disadvantages such as the antigens transfer, the need for invasive surgery, donor site morbidity, limited available bone, and absorption of the bone graft.  Furthermore, the use of mechanical devices or artificial organs have limitations because of the risk of infection, obstruction of the blood flow, and the low durability.  Thus, tissue engineering based on different scaffolds and cells has been developed for the repair and restoration of damaged skeletal system. ,
Bio ceramics, polyesters, and hydrogels are used as drugs or growth factor deliveries and as scaffolds in bone tissue engineering. ,,,
Although polyesters have better mechanical properties, they produce acidic materials and cause inflammation. , In contrast, bioceramics such as hydroxyapatite and tricalcium phosphate (HA-TCP) display excellent osteoconductive properties and could be designed in the appropriate shape and size without any inflammation and rejection following transplantation. ,,, Moreover, implanted bioceramics in contact with bone matrix and cells induces repair of damaged and degenerated tissues.  The choice of suitable cell source cell is vital for the engineering of bone tissue. The ethical issues and the poor known characteristics limit the use of embryonic stem cells and induced pluripotent stem cells. 
Adipose tissue is an attractive source for stem cells.  Adipose-derived stem cells (ADSCs) are multi potent which can differentiate into variety of cell lineages.  ADSCs have various advantages over the bone marrow mesenchymal stem cells (MSCs) such as the ease of accessibility, the abundance in number, high proliferation rate, and no need to preserve for long time in cell banks. ,,
Studies have demonstrated that ADSCs could be differentiated into bone cells and produce organic and mineralized extracellular matrix and alkaline phosphatase enzyme in vitro.  Auto and allograft transplant of ADSCs is possible without the risk of rejection or transfer of contagious diseases due to their lack of HLA-DR antigens.  Some researchers have reported the benefits of ADSCs-scaffold constructs, such as collagen and alginate scaffold, in regenerative medicine. ,
In this study, the repair of tibial defects in animal model was investigated with differentiated osteoblasts from ADSCs in HA-TCP scaffold in comparison to the cell-free HA-TCP.
| Methods|| |
Adipose tissue harvesting
In this experiment, six healthy dogs with average weight of 20-35 kg were used. Ethical principles in animal researches were considered. Ketamine (15 mg/kg) (Alfasan, Holland) and xylazine 2 mg/kg intramuscular with orotracheal intubation were used for anesthesia followed by respiratory administration of halothane and N 2 O. After injecting local anesthesia with lidocaine 2% plus epinephrine 1:100,000, an incision with a length of 5 cm was performed in cervical area. After dissection, about 20 g subcutaneous fats were harvested and maintained in phosphate-buffered saline (PBS) (Sigma).
Isolation of adipose-derived stem cells
Canine ADSCs were isolated according to previous protocol.  Fat tissue was washed with PBS (Sigma) and digested with Type I collagenase enzyme (1 mg per 1 g tissue) at 37°C for 30 min. After centrifuge, cell pellet resuspended and cultured in Dulbecco modified eagle medium (DMEM) (Gibco®) supplemented with fetal bovine serum 10% (Gibco®) and penicillin-streptomycin 1% (Gibco®). Nonadherent cells were removed from culture by medium changing. Hence, adherent cells were expanded as monolayer cultures at 5% CO 2 with a temperature of 37°C. Medium was changed twice every week.
After expansion in the control medium, 5 × 10 6 cells/ml ADSCs were seeded onto witted HA-TCP blocks scaffold which were purchased from Ceraform Co., Germany, in the size of 3 mm × 3 mm × 3 mm (35-65%) and cultured in osteogenic medium. The osteogenic medium contained DMEM, 10% fetal bovine serum, 10 mM b-glycerol-3-phosphate (Sigma), 10 nM dexamethasone (Sigma), 100 mg/ml L-ascorbic acid (Sigma), and 1% penicillin/streptomycin. The medium was replaced every 3 days and after 14 days, scaffold/cell investigated by scanning electron microscopy (SEM) and reverse transcription polymerase chain reaction (RT-PCR).
Scanning electron microscopy
The blocks of HA-TCP/cell were washed with PBS and fixed with glutaraldehyde 2.5% for 2 h. Then, blocks were dehydrated by ascending ethanol and coated by thin layer of gold by sputter coater. Prepared samples were visualized by SEM (Philips XL 30).
In vivo implantation and specimen harvesting
The canines were anesthetized and after sterilization of skin, tibia bone was exposed and two cylindrical defected sites in 10 mm diameter were created on the anterior aspect of tibia by trephine bur (Meisinger, Dusseldorf, Germany) [Figure 1].
|Figure 1: (a) Cylindrical defects on the anterior aspect of tibia by trephine bur. (b) After 8 weeks, biopsies from repaired sites were removed for histological evaluation|
Click here to view
The defected sites were filled with HA-TCP contained differentiated cells as the test group and without cells as the cell-free group and marked with titanium screw. The wound was closed in layered fashion (Vicryl 3.0, GmbH and Co., KG - Norderstedt, Germany). After the surgery, animals received ceftriaxone 1 g intravenous (Loghman pharmaceutical and Hygienic Co.) daily for 5 days.
After 8 weeks similar to previous surgery, animals were anesthetized and prepared for surgery. Biopsies were applied by a larger trephine bur (12.0 mm) and used for histological, immunohistochemical (IHC) methods, and densitometry test.
Reverse transcription polymerase chain reaction analysis
The expression of specific bone markers (Type I collagen and osteocalcin) was proved with RT-PCR. Cells RNAs isolated by RNX-plus Isolation Kit (CinnaGen Inc., Iran); cDNA was synthesized from extracted RNA using First-strand cDNA Synthesis Kit (Frementase). For PCR reaction, cDNA, dNTPs, PCR buffer, Taq DNA polymerase, and primers (Frementase) were used.
PCR reaction mixture contained 2.5 μl cDNA, 1 × PCR buffer (AMS), 200 μM dNTPs, 1 unit Taq DNA Polymerase (Fermentas), and 0.5 μM of each primer (osteocalcin: forward 5'-ACACTCCTCGCCCTATTG -3'; reverse 5'- GATGTGGTCAGCCAACTC- 3', 371 bp, Type I collagen: forward, 5'- ACTTAGAGTATCTATAAACTTGATACTC- 3', reverse, 5'- TAAATTGTTACTAAGCATATTATAATTAACATC -3'599 bp).
For amplification, initial denaturation at 95°C for 5 min followed by 35 cycles of 93°C, 65°C, and 72°C for 30, 45, and 40 s, respectively. The PCR results were determined in 1% agarose gel and then stained by ethidium bromide staining and visualized by UV trans-illuminator. After fixation of samples in neutral buffered formalin 10% and decalcification by using of EDTA solution, samples were dehydrated with ethyl alcohol, cleared with xylene, and embedded with paraffin. These blocks were sectioned with microtome at 5 μm thickness. Sections were stained with hematoxylin and eosin. In addition, trichrome mallory staining was done as described.  In this procedure, the sections stained in acid fuschin 1% (Merck) solution and then aniline blue 0.5% (Merck), orange G 2% (Merck), and oxalic acid 2% (Sigma) in distilled water. 
For antigen retrieval, the specimens were deparaffinized and treated with citrate buffer 0.01 mol/l, pH 6.0 (Merck), heated at 100°C for 6 × 2 min.
For blocking of endogenous peroxidase, sections were incubated in H 2 O 2 3% for 10 min. The mouse monoclonal antibody against osteopontin (1:300 concentration; Santa Cruz Biotechnology, USA) was used at 4°C overnight. Then, specimens were incubated in secondary antibody conjugated with horse radish peroxidase (Abcam) for 30 min. After staining with diaminobenzidine (Sigma), hematoxylin dye was used to counter staining.
Some of the biopsy samples were placed in acrylamide mold for analyzing their average strength and evaluated by "Tensometer Universal" equipment. Then, the rates of strength were compared with normal tissues and the control group.
All data were considered as means and standard deviation. The data were subjected to statistical analysis using the Wilcoxon test. Differences at P < 0.05 were considered significant in this study.
| Results|| |
The canine ADSCs in third passage were observed with spindle fibroblast-like cells within a homogeneous monolayer culture [Figure 2].
|Figure 2: Subcutaneous adipose-derived stem cells in third passage (×40)|
Click here to view
For induction of osteogenic differentiation, ADSCs of third passage were seeded in HA-TCP scaffold and were cultured in osteogenic medium. SEM results represented that the stem cells have adhered in the pores of the scaffold and their processes extended and connected together [Figure 3]a.
|Figure 3: Scanning electron microscopy technique: (a) Stem cells adhered in the pores of scaffold (b) extracellular matrix as deposition of granular products secreted by differentiated osteoblasts in the pores of hydroxyapatite/tricalcium phosphate scaffold|
Click here to view
Osteoblasts secreted extracellular matrix as deposition of granules after osteogenesis induction [Figure 3]b.
Reverse transcription polymerase chain reaction result
RT-PCR results indicated the expression of Type I collagen and osteocalcin genes in differentiated osteoblasts derived from ADSCs. Glyceraldehyde-3-phosphate dehydrogenase as a housekeeping gene has been expressed in all cells [Figure 4].
|Figure 4: Expression of Type I collagen and osteocalcin genes in differentiated osteoblasts derived from adipose-derived stem cells. Glyceraldehyde-3-Phosphate Dehydrogenase as a housekeeping gene had expressed in all groups|
Click here to view
Evaluation of tissue sections revealed the formation of bone trabeculae and lacunae. This histological evaluation showed that the bone trabecular and the mineral matrices were thicker in the test group rather than the cell-free group [Figure 5] and [Figure 6].
|Figure 5: Formation of bone tissue with trabeculae in bone defects. (a) Cell-free group, (b) test group (H and E, ×100)|
Click here to view
|Figure 6: Trichrome mallory staining indicated the existence of Type I collagen in bone matrix in both groups. (a) Cell-free group (b) test group (×100)|
Click here to view
Analysis of IHC results showed the existence of osteopontin glycoprotein in the matrix of two groups, which is considered as an important bone marker [Figure 7].
|Figure 7: Analysis of intracerebral hemorrhage for production of osteopontin|
Click here to view
Densitometry method indicated that the strength in the test group was approximately similar to the cell-free group and natural bone (P > 0.05) [Figure 8].
|Figure 8: The rates of strength were evaluated between hydroxyapatite/tricalcium phosphate with osteoblast, hydroxyapatite/tricalcium phosphate without cells and natural bone tissue via densitometry|
Click here to view
| Discussion|| |
In this study, we evaluated the ability of the differentiated osteoblasts, obtained from ADSCs and seeded into HA-TCP, to repair the bone defects in comparison to HA-TCP alone and natural bone.
Our results indicated that the thickness of the bone trabecular was more in the test group compared to the cell-free group. The production of osteopontin in the extracellular matrix was observed in both groups. The bone strength in the test group was similar to the cell-free group and natural bone as shown by the densitometry.
Stem cell-derived osteoblasts play an important role in the bone tissue engineering which were considered by researchers. ,, The final aim of tissue engineering is to regenerate new tissues via mediators, scaffolds, and biological matrices. Different natural and synthetic scaffolds were used for tissue engineering in the bone repair. ,,,, However, scaffolds with similarities to the bone matrix could provide a suitable microenvironment for MSCs adhesion, proliferation, and differentiation in osteogenesis. ,,
Hydroxyapatite is an important element of the bones; regarding chemical structure and physical properties, it is similar to the natural bone and it is appropriate for bone tissue engineering. ,
Hydroxyapatite composed by tricalcium phosphate (HA-TC) has been used with different HA to TCP ratios, but bone formation was detected only in HT73 (HA to TCP ratio, 7-3) specimens. 
Rathbone et al. reported that HA increased the density of the bone mineral of defected radius compared to controls in a rabbit model.  Another study compared cellseeded HA scaffolds by bone marrow stem cell and HA scaffolds without cell in the bone regeneration after 8 weeks, they showed no difference in bone formation between two groups.
Our study showed that the thickness of the bone trabecular was more in bone defects implanted by HA-TCP with differentiated osteoblasts (from ADSC) compared to the cell-free scaffolds. The presence of cells in HA-TCP scaffold increased the production of the mineral matrix. The strength of the HA-TCP scaffold with differentiated osteoblasts was significantly more than the cell-free HA-TCP
Kim et al. indicated that autologous osteoblasts produce more mineral matrix than the autologous bone marrow-derived MSCs in a rabbit radial defect model.  In our study, differentiated osteoblasts from ADSC produced mineral matrix similar to natural bone, thus differentiation of stem cells to osteoblasts in vitro could compensate the limitation of mineral matrix production by undifferentiated stem cells, as shown in Kim's study. Thus, the status of used stem cells can affect the results differently.
In addition, Pourebrahim et al. compared an autograft corticocancellous tibial to HA-TCP differentiated osteoblasts from ADSCs, in the defects of maxillary bone, they observed that the bone formation is higher in autograft group.  However, we compared HA/TCP-differentiated osteoblasts from ADSCs to cell-free HA/TCP in tibia defect and natural bone and showed that formation of bone trabeculae in HA/TCP-differentiated osteoblasts group was more than the cell-free group but less than natural bone while the strength was similar in all groups.
| Conclusions|| |
Our results indicated that HA-TCP scaffold provides a suitable environment for the differentiation and activity of osteoblasts. Furthermore, differentiated osteoblasts from ADSCs seeded into HA-TCP could be regarded as appropriate factors for bone tissue engineering.
This research was supported by Isfahan University of Medical Sciences. This manuscript is resulted from project with number: 389334. Hence, has a specific ethic committee.
Financial support and sponsorship
Conflicts of interest
There are no conflicts of interest.
| References|| |
Cancedda R, Dozin B, Giannoni P, Quarto R. Tissue engineering and cell therapy of cartilage and bone. Matrix Biol 2003;22:81-91.
Green SA, Jackson JM, Wall DM, Marinow H, Ishkanian J. Management of segmental defects by the Ilizarov intercalary bone transport method. Clin Orthop Relat Res 1992;(280):136-42.
LaRossa D, Buchman S, Rothkopf DM, Mayro R, Randall P. A comparison of iliac and cranial bone in secondary grafting of alveolar clefts. Plast Reconstr Surg 1995;96:789-97.
Schantz JT, Hutmacher DW, Lam CX, Brinkmann M, Wong KM, Lim TC, et al.
Repair of calvarial defects with customised tissue-engineered bone grafts II. Evaluation of cellular efficiency and efficacy in vivo
. Tissue Eng 2003;9 Suppl 1:S127-39.
Alsberg E, Anderson KW, Albeiruti A, Franceschi RT, Mooney DJ. Cell-interactive alginate hydrogels for bone tissue engineering. J Dent Res 2001;80:2025-9.
Cai X, Lin Y, Ou G, Luo E, Man Y, Yuan Q, et al.
Ectopic osteogenesis and chondrogenesis of bone marrow stromal stem cells in alginate system. Cell Biol Int 2007;31:776-83.
Stevens MM, Marini RP, Schaefer D, Aronson J, Langer R, Shastri VP. In vivo
engineering of organs: The bone bioreactor. Proc Natl Acad Sci U S A 2005;102:11450-5.
Freihofer HP, Borstlap WA, Kuijpers-Jagtman AM, Voorsmit RA, van Damme PA, Heidbüchel KL, et al.
Timing and transplant materials for closure of alveolar clefts. A clinical comparison of 296 cases. J Craniomaxillofac Surg 1993;21:143-8.
Hughes CW, Revington PJ. The proximal tibia donor site in cleft alveolar bone grafting: Experience of 75 consecutive cases. J Craniomaxillofac Surg 2002;30:12-6.
Gordana VN, Frenshney R. Culture of Cell for Tissue Engineering. Wiley, Inc; 2006. p. 412-22.
Fuchs JR, Nasseri BA, Vacanti JP. Tissue engineering: A 21 st
century solution to surgical reconstruction. Ann Thorac Surg 2001;72:577-91.
Hutmacher DW. Scaffolds in tissue engineering bone and cartilage. Biomaterials 2000;21:2529-43.
Saito N, Okada T, Horiuchi H, Murakami N, Takahashi J, Nawata M, et al.
A biodegradable polymer as a cytokine delivery system for inducing bone formation. Nat Biotechnol 2001;19:332-5.
Chen G, Ushida T, Tateishi T. Poly (DL-lactic-co-glycolic acid) sponge hybridized with collagen microsponges and deposited apatite particulates. J Biomed Mater Res 2001;57:8-14.
George J, Onodera J, Miyata T. Biodegradable honeycomb collagen scaffold for dermal tissue engineering. J Biomed Mater Res A 2008;87:1103-11.
Alsberg H, Yang Z. Regulating bone formation via controlled scaffold degradation. J Bone Miner Res 2003;18:923-9.
Kim EH, Heo CY. Current applications of adipose-derived stem cells and their future perspectives. World J Stem Cells 2014;6:65-8.
Hashemibeni B, Esfandiari E, Razavi SH. Effect of TGF-β3 and BMP-6 growth factors on chondrogenic differentiation of adipose-derived stem cells in alginate scaffold. J Iran Anat Sci 2010;8:1-5.
Hashemibeni B, Razavi S, Esfandiari E, Karbasi S, Mardani MO. Human cartilage tissue engineering from adipose-derived stem cells with BMP-6 in alginate scaffold. J Iran Anat Sci 2010;8:117-29.
Colter DC, Sekiya I, Prockop DJ. Identification of a subpopulation of rapidly self-renewing and multipotential adult stem cells in colonies of human marrow stromal cells. Proc Natl Acad Sci U S A 2001;98:7841-5.
Kassem M, Kristiansen M, Abdallah BM. Mesenchymal stem cells: Cell biology and potential use in therapy. Basic Clin Pharmacol Toxicol 2004;95:209-14.
Bischoff FZ, Hahn S, Johnson KL, Simpson JL, Bianchi DW, Lewis DE, et al.
Intact fetal cells in maternal plasma: Are they really there? Lancet 2003;361:139-40.
Lee RH, Kim B, Choi I, Kim H, Choi HS, Suh K, et al.
Characterization and expression analysis of mesenchymal stem cells from human bone marrow and adipose tissue. Cell Physiol Biochem 2004;14:311-24.
Haghighat A, Akhavan A, Hashemi-Beni B, Deihimi P, Yadegari A, Heidari F. Adipose derived stem cells for treatment of mandibular bone defects: An autologous study in dogs. Dent Res J (Isfahan) 2011;8 Suppl 1:S51-7.
Hashemibeni B, Esfandiari E, Sadeghi F, Heidary F, Roshankhah S, Mardani M, et al.
An animal model study for bone repair with encapsulated differentiated osteoblasts from adipose-derived stem cells in alginate. Iran J Basic Med Sci 2014;17:854-9.
Fulin C, Xiaobin C. Bone marrow-derived osteoblasts seeded into porous beta-tricalcium phosphate to repair segmental defect in canine's mandibula. J Trauma Emerg Surg 2006;12:265-75.
Zuk PA, Zhu M, Ashjian P, De Ugarte DA, Huang JI, Mizuno H, et al.
Human adipose tissue is a source of multipotent stem cells. Mol Biol Cell 2002;13:4279-95.
Li Z, Ramay HR, Hauch KD, Xiao D, Zhang M. Chitosan-alginate hybrid scaffolds for bone tissue engineering. Biomaterials 2005;26:3919-28.
Mohan BG, Suresh Babu S, Varma HK, John A. In vitro
evaluation of bioactive strontium-based ceramic with rabbit adipose-derived stem cells for bone tissue regeneration. J Mater Sci Mater Med 2013;24:2831-44.
Linero IM, Doncel A, Chaparro O. Proliferation and osteogenic differentiation of mesenchymal stem cells in hydrogels of human blood plasma. Biomedica 2014;34:67-78.
Appleford MR, Oh S, Oh N, Ong JL. In vivo
study on hydroxyapatite scaffolds with trabecular architecture for bone repair. J Biomed Mater Res A 2009;89:1019-27.
Hosseinzadeh E, Davarpanah M, Hassanzadeh Nemati N, Tavakoli SA. Fabrication of a hard tissue replacement using natural hydroxyapatite derived from bovine bones by thermal decomposition method. Int J Organ Transplant Med 2014;5:23-31.
El Backly RM, Zaky SH, Canciani B, Saad MM, Eweida AM, Brun F, et al.
Platelet rich plasma enhances osteoconductive properties of a hydroxyapatite-ß-tricalcium phosphate scaffold (Skelite) for late healing of critical size rabbit calvarial defects. J Craniomaxillofac Surg 2014;42:e70-9.
Kurashina K, Kurita H, Wu Q, Ohtsuka A, Kobayashi H. Ectopic osteogenesis with biphasic ceramics of hydroxyapatite and tricalcium phosphate in rabbits. Biomaterials 2002;23:407-12.
Alam MI, Asahina I, Ohmamiuda K, Takahashi K, Yokota S, Enomoto S. Evaluation of ceramics composed of different hydroxyapatite to tricalcium phosphate ratios as carriers for rhBMP-2. Biomaterials 2001;22:1643-51.
Guda T, Walker JA, Pollot BE, Appleford MR, Oh S, Ong JL, et al. In vivo
performance of bilayer hydroxyapatite scaffolds for bone tissue regeneration in the rabbit radius. J Mater Sci Mater Med 2011;22:647-56.
Rathbone CR, Guda T, Singleton BM, Oh DS, Appleford MR, Ong JL, et al.
Effect of cell-seeded hydroxyapatite scaffolds on rabbit radius bone regeneration. J Biomed Mater Res A 2014;102:1458-66.
Kim SJ, Chung YG, Lee YK, Oh IW, Kim YS, Moon YS. Comparison of the osteogenic potentials of autologous cultured osteoblasts and mesenchymal stem cells loaded onto allogeneic cancellous bone granules. Cell Tissue Res 2012;347:303-10.
Pourebrahim N, Hashemibeni B, Shahnaseri S, Torabinia N, Mousavi B, Adibi S, et al.
A comparison of tissue-engineered bone from adipose-derived stem cell with autogenous bone repair in maxillary alveolar cleft model in dogs. Int J Oral Maxillofac Surg 2013;42:562-8.
[Figure 1], [Figure 2], [Figure 3], [Figure 4], [Figure 5], [Figure 6], [Figure 7], [Figure 8]
|This article has been cited by|
||Biological Aging Parameters Can Be Improved After Autologous Adipose-Derived Stem Cell Injection
| ||Hye-Youn Son,Hahn-Sol Bae,Youngsook Son,Sundong Kim,Hyun-Sook Hong,Ji-Ung Park |
| ||Journal of Craniofacial Surgery. 2019; 30(3): 652 |
|[Pubmed] | [DOI]|
||Doping ß-TCP as a Strategy for Enhancing the Regenerative Potential of Composite ß-TCP—Alkali-Free Bioactive Glass Bone Grafts. Experimental Study in Rats
| ||Manuel Ferreira,Ana Brito,Daniela Brazete,Inês Pereira,Eunice Carrilho,Ana Abrantes,Ana Pires,Maria Aguiar,Lina Carvalho,Maria Botelho,José Ferreira |
| ||Materials. 2018; 12(1): 4 |
|[Pubmed] | [DOI]|
||Biological properties of calcium phosphate biomaterials for bone repair: a review
| ||Jingyi Lu,Huijun Yu,Chuanzhong Chen |
| ||RSC Advances. 2018; 8(4): 2015 |
|[Pubmed] | [DOI]|
||Calcium-infiltrated Biphasic Hydroxyapatite Scaffolds for Human Hematopoietic Stem Cell Culture
| ||Qinghao Zhang,Joerg C Gerlach,Ian Nettleship,Eva Schmelzer |
| ||Tissue Engineering Part A. 2018; |
|[Pubmed] | [DOI]|
||Effect of Calcium-Infiltrated Hydroxyapatite Scaffolds on the Hematopoietic Fate of Human Umbilical Vein Endothelial Cells
| ||Qinghao Zhang,Jörg C. Gerlach,Eva Schmelzer,Ian Nettleship |
| ||Journal of Vascular Research. 2017; 54(6): 376 |
|[Pubmed] | [DOI]|